Chemical Resistance
All chemical tests listed have been successfully passed on painted metal and plastic material.
Plastic components are subjected to 90 days exposure tests with the following chemicals:

• 3% H2SO4 (sulfuric acid)
• 0.2N NaOH (sodium hydroxide)
• NH3 (ammonia)
• 90% Isopropyl Alcohol
• Kerosene

Flammability Testing
Flammability tests are conducted per UL 94 Type 5V on actual production parts.

QUV Testing
QUV weathering tests:
8 hour cycles at 70°F lighted, 4 hours dark with condensation at 50°F, testing was conducted about every 1,000 hours. No part degradation or plastic parts has occurred following 5,000 hours of testing.

Thermal Cycling
Production plastic pedestals have been exposed to the following conditions:

• Initial Temperature = ambient 21°- 23°C
• Heating to 75°C and held for 3.6 hours
• Cooling to -23°C and held for 3.6 hours
• Held at -23°C for 65 hours
• Heating to 73°C and held for 7 hours
• Cooling to -23°C and held for 47 hours

Form, Fit and Functional inspections were performed after each cycle with no concerning issues.

Impact Resistance
Production models are regularly tested at impact forces up to 170ft-lbs.
Cold impact tests are performed up to 100ft-lbs.

SPEC SHEETS

• CVK-101035A Universal Split Base 10X10 HDPE Pedestal
• FSPL1212 Series Universal Solid Base 12x12 HDPE Pedestals
• FSPL183117 series of Universal Solid Base 18” X 31”X17” HDPE Pedestals
• FSPL1431 series of Universal Solid Base 14” X 31” HDPE Pedestals

CONTACT US for Purchasing Information!