Adhesives
Adhesives
Manufactured Products
 
Adhesives For Fiber Fixing
(AT8105, AT9575M)


Fig. Typical Fiber Array

Main properties for fixing optical fiber
(AT8105 (Acrylate), AT9575M (Epoxy) )

Name (Main Components)

 

AT8105 (Acrylate)

 

AT9575M (Epoxy)

Conditions

External appearance

 

Light amber

 

Light amber

Viscosity (cP)

 

>20,000 (Paste)
[25]

 

>27,000 (Paste)
[25]

Curing

Curing Time (min)

 

5 *1

 

10 *2

Shrinkage during curing (%)

 

6

 

4

Properties after curing

Glass Transition Temperature ()

 

99

 

34

Modulus ( dyn/cm2) [25]          

 

-

 

5.1 / 0.43

Optical transmittance (%)
[ = 1.3m, 1mm]

 

-

 

62

Thermal expansion coefficient
( )

 

-

 

8~9

Adhesion Strength
(kgf/cm2)[Glass]

 

>200

 

>146


(Note)
This property data is a measured value on samples instead of the guaranteed value.
Recommended curing process :

*1 UV irradiation : 10mW/cm2 (365nm) Heat treatment : 50 ~ 60 for 30 ~ 60min
*2 UV irradiation : 30mW/cm2 (365nm) Heat treatment : 100 for 2h

 